Antimicrobial gas impregnated devices and methods

ABSTRACT

A nitric oxide gas-releasing conduit configured for surgical implantation through a patient&#39;s tympanic membrane. The nitric oxide gas-releasing conduit comprises a gas-permeable cured resin material configured for releasably sequestering therein gas. The gas-permeable cured resin material is charged with nitric oxide gas. The nitric oxide gas-releasing conduit may be optionally coated with an antimicrobial gas-releasing composition. The gas-releasing coating composition may be configured to release nitric oxide.

This application is a Continuation of U.S. patent application Ser. No. 12/234,599, filed Sep. 19, 2008, which claims priority from U.S. Provisional Application No. 60/974,228, filed Sep. 21, 2007, all of which are incorporated herein by reference in their entirety.

BACKGROUND

Installation of tympanostomy tubes for the treatment of otitis media with effusion or in patients with recurrent events of acute otitis media, is a commonly performed surgical procedure in North America and elsewhere. In this procedure an incision is made in the tympanic membrane, fluid from within the middle ear is aspirated and a tympanostomy tube is inserted. The tubes can have various configurations and materials, and are effective in correcting the hearing loss due to the effusion as long as the tubes are in place in the ear. The materials which can be used to make tympanostoray tubes include thermoplastics such as modified elastomers and olefins, thermosets such as silicone and polytetrafluoroethylene; and metals such as stainless steel and titanium. Children with persistent middle ear effusions who do not respond to antibiotics undergo a procedure in which a myringotomy is performed in the tympanic membrane under local anesthesia. However the implantation of the tympanostomy tubes also be done under general anesthesia.

Purulent otorrhea frequently develops after tube insertion. In one study by H. G. Birck and J. J. Mravek “Myringotomy for Middle Ear Effusions,” Ann. of Otol. Rhino. Laryngo., volume 85, pages 263-267 (1979), the investigators observed that 15% of children having tympanostomy tubes inserted in their ears following myringotomy developed postoperative otorrhea. In a more recent study by George A. Gates et al., “Post Tympanostomy Otorrhea,” Laryngoscope, volume 96, pages 630-634, (June 1986), the investigators observed that the incidence of tympanostomy tube induced otorrhea following myringotomy was 18%. In a clinical study performed by Balkany et al., “A Prospective Study of Infection Following Tympanostomy and Tube Insertion,” American Journal of Otology, volume 4, pages 288-291 (1983), the investigators observed an incidence of postoperative otorrhea of 19% in children receiving tympanostomy tubes with no antibiotic drops postoperatively applied. In the Balkany et al. study, the investigators found that the incidence of postoperative otorrhea was reduced to 6% when antibiotic drops were put into the patient's ear after myringotomy. In another study on the use of antibiotics after myringotomy, R. S. Baker and R. A. Chole, “A Randomized Clinical Trial of Topical Gentamicia After Tympanostomy Tube Placement,” Arch. Otolaryngology Head and Neck Surgery, volume 114, pages, 755-757 (July 1988), the investigators found that the incidence of infections in the experimental group using Gentamicin, an ophthalmic solution used as otic drops, had an incidence of infection significantly reduced by antibiotic drops.

In both the Balkany et al. and Baker et al. studies using antibiotic drops after tympanostomy, the investigators used potentially ototoxic antibiotics, namely Cortisporin and Gentamicin. Based on their frequency of use, and the lack of adverse effects noted in these studies, antibiotic drops are now used routinely to prevent postoperative otorrhea. However, thorough studies demonstrating the absence of adverse toxicological reaction in the use of antibiotic drugs for the treatment of postoperative otorrhea have not been published.

In addition to the relatively high incidence of otorrhea after myringotomy, investigators have observed children with implanted tympanostomy tubes sometimes experience bouts of otorrhea. Occasionally, the otorrhea became persistent causing some investigators to believe that the tympanostomy tubes become colonized with pathogenic bacteria.

The relatively high incidence of otorrhea after myringotomy and tympanostomy tube insertion exposes patients with persistent middle ear effusions to significant morbidity and additional treatment time and cost.

It would be desirable to utilize tympanostomy tubes whereby the incidence of otorrhea and other microbial induced infection after myringotomy and tympanostomy tube insertion could be substantially reduced without the use of antibiotics and the potential ototoxic reaction associated with the use of such drugs.

One approach for reducing bacterial infection encountered with the use of medical devices inserted into body cavities has been to apply an antimicrobial coating to the surface of the medical device. For example, U.S. Pat. No. 4,592,920 to Murtfeldt; U.S. Pat. No. 4,603,152 to Laurin et al. and U.S. Pat. No. 4,677,143 to Laurin et al. each teach applying a coating containing an antimicrobial agent such as silver oxide to the outer surfaces of medical devices such as catheters, enteral feeding tubes, endotracheal tubes and other hollow tubular devices.

U.S. Pat. No. 4,592,920 to Murtfeldt is primarily concerned with providing a surface coating of an antimicrobial metal compound on a medical device such as a catheter, but also discloses that the metal compound can be “imbedded” within the entire catheter. However, the Murtfeldt patent finds the imbedded construction to be less desirable since the antimicrobial metal compound imbedded within the side wall of the catheter has less likelihood of encountering migrating microbes and by inference is less effective than a surface coating.

U.S. Pat. No. 6,361,526 provides a tube formed from a thermoset resin containing therein between 0.5 to 15% by weight of a selected antimicrobial metal oxide compounds exemplified by silver oxide, that are capable of migrating to the sidewall surfaces of the tube. Such metal oxide-laden antimicrobial resin-based tubes are generally produced by controllably intermixing a selected metal oxide into a thermoset resin paste that is subsequently milled, then formed into a hollow tube by conventional tube-forming processes.

SUMMARY

In certain embodiments, ear drainage tubes are provided, including gas releasing antimicrobial ear drainage tubes. Exemplary embodiments of the present invention, are directed to antimicrobial gas-permeable gas-releasing conduits suitable for surgical implantation into and through patients' tympanic membranes. Suitable gas-permeable conduits are exemplified by tympanostomy tubes, myringotomy tubes and the like.

According to one aspect, the cured gas-permeable gas-releasing resin material comprises curable silicones.

According to another aspect, the antimicrobial gas-permeable gas-releasing molecules are exemplified by nitric oxide (NO) molecules.

According to another aspect the NO gas-permeable gas-releasing implantable conduits are coated with NO-releasing compositions exemplified by those having N₂O₂ ⁻ functional groups, NO-releasing intramolecular salts, and S-nitrosothiols among others.

According to further aspect, the antimicrobial gas-permeable gas-releasing conduits are exemplified by tympanostomy tubes.

According to a further aspect, the antimicrobial gas-permeable gas-releasing conduits are exemplified by myringotomy tubes.

According to another exemplary embodiment of the present invention, the antimicrobial gas-permeable gas-releasing conduits are produced with a process whereby fully configured and cured gas-permeable resin-based tubes are controllably saturated with a selected antimicrobial gas exemplified by NO, whereby the resin-based tubes releasably sequester NO gas molecules. The antimicrobial gas-saturated conduits are individually packaged in gas-impermeable containers.

According to one aspect, the resin-based conduits sequestering therein NO gas molecules, are coated with NO-releasing compositions exemplified by those having N₂O₂ ⁻ functional groups, NO-releasing intramolecular salts, and S-nitrosothiols among others.

According to a further embodiment, the antimicrobial gas-releasing conduits are produced by intermixing a suitable selected chelating agent saturated with antimicrobial gas molecules, with a curable polymeric resin material. The intermixed material is formed and configured into a plurality of antimicrobial gas-releasing conduits, then cured. After curing, the antimicrobial gas-releasing conduits are individually packaged and sealed into gas-impermeable containers.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be described in conjunction with reference to the following drawings, in which:

FIG. 1(a) is a chart showing the effects of gNO released from gNO-charged vent tubes on the proliferation of Streptococcus pyogenes. FIG. 1(b) is a chart showing the effects of released gNO on survival of S. pyogenes;

FIG. 2(a) is a chart showing the effects of gNO released from gNO-charged vent tubes on the proliferation of Streptococcus pneumonia. FIG. 2(b) is a chart showing the effects of released gNO on survival of S. pneumonia;

FIG. 3(a) is a chart showing the effects of gNO released from gNO-charged vent tubes on the proliferation of Moraxella catarrhalis. FIG. 3(b) is a chart showing the effects of released gNO on survival of M. catarrhalis;

FIG. 4(a) is a chart showing the effects of gNO released from gNO-charged vent tubes on the proliferation of Haemophilus influenzae. FIG. 4(b) is a chart showing the effects of released gNO on survival of H. influenzae;

FIG. 5(a) is a chart showing the effects of gNO released from gNO-charged vent tubes on the proliferation of methicillin-resistant Staphylococcus aureus. FIG. 5(b) is a chart showing the effects of released gNO on survival of S. aureus; and

FIG. 6 is a chart showing the effects of gNO released from gNO-charged silicon vent tubes and gNO-charged polytetrafluoroethylene vent tubes on the proliferation of Staphylococcus aureus.

FIG. 7 provides a schematic illustration of an embodiment of the presently described conduit, wherein a hollow tube 1 can be coated on the outer surface 2 with a coating comprising antimicrobial gas-releasing coating.

DETAILED DESCRIPTION

Certain exemplary embodiments of the present invention are directed to antimicrobial conduit structures configured for long-term installation through the tympanic membranes into the inner ear cavities for the purpose of draining fluids therefrom. Such conduit structures are exemplified by tympanostomy tubes, myringotomy ventilation tubes and the like, and will be generally referred to from hereon in as “tympanostomy tubes.” The antimicrobial tympanostomy tubes generally comprise materials that are controllably permeatable with gases selected for their antimicrobial properties.

The antimicrobial tympanostomy tubes are characterized by their biological compatibility with otologic tissue associated with the tympanic membrane and middle ear tissues, and generally comprise polymeric materials exemplified by resins which after Forming and curing, are microporous and have the requisite high gas permeability properties needed to prepare the antimicrobial tympanostomy tubes. These resins are suitably characterized by an ability for infiltratably sequestering selected permeating antimicrobial gases, and then controllably releasing the antimicrobial gases over extended periods of time. Suitable resins are exemplified by curable silicones, polyvinyl acetates, thermoplastic elastomers, acrylonitrile-butadiene-styrene copolymer rubber, polyurethanes and the like. In certain embodiments, curable silicone resins are preferred for the manufacture of the antimicrobial tympostomy tubes due to their molecular structure which provides good flexibility both microscopically and macroscopically, and high gas permeability rates. Table 1 illustrates the gas permeability of silicone resins in comparison with other types of materials suitable for such tubular manufacture.

The geometries of the antimicrobial tympanostomy tubes are generally cylindrical and may simply comprise elongate hollow conduits having the same diameter extending from end to end, or alternatively may comprise elaborate configurations that may additionally include abrupt diameter changes and odd shaped flanges.

TABLE 1 Gas permeation through selected materials (cc/0.001 in/100.0 in²/24 h at 22.8° C., 0% relative humidity, ASTM D-1434)*. Permeating gas Tubular material O₂ CO₂ Silicone 50,000 300,000 Urethanes 200 3,000 Epoxies 5-10 8 Fluorocarbons 7-15 15-30 Nylon 2.6 4.7 Polybutylene 385 825 Polycarbonate 258 775 Cellulose acetate 23 105 *adapted from; (1) Packaging Encyclopedia 1988 Vol. 33 No. 5, pp. 54-55, and Machine Design, May 25, 1967, p. 192.

Gaseous nitric oxide (gNO) is an intermediary compound produced during the normal functioning of numerous biochemical pathways in many biological systems including humans. gNO is known to those skilled in these arts as a key biological messenger signaling compound that plays key roles in many biological processes. Recent evidence (e.g., Ghaffari et al., 2005 Nitric Oxide 14: 21-29) suggests that gNO plays an important role in mammalian host defense against infection and regulates wound healing and angiogenesis. In particular, topical applications of exogenous gNO at 200 ppm for extended periods of time inhibited and prevented the growth of a wide range of microbial pathogens Staphylococcus aureus, Escherichia coli, Group B Streptococcus, Pseudomonas aeruginosa, and Candida albicans, without any cytotoxic effects on cultured human dermal fibroblasts. Furthermore, McMullin et al. (2005, Respir. Care 5:1451-1456) demonstrated that exogenous gNO at a concentration of 200 ppm could clear nosocomial pneumonia caused by microbial pathogens such as S. aureus and P. aeruginosa, in about 6 hours. Accordingly, gNO is a particularly suitable antimicrobial gas for saturatingly permeating tympanostomy tubes comprising gas-permeable polymeric materials.

The antimicrobial typanostomy tubes described herein may be produced by first casting a desired tubular configuration with a selected suitable resin using conventional methods known to those skilled in these arts. It is suitable to process the tubes into their final configuration and finish after which, the tubes are placed into a sealable chamber. The chamber is then saturated with a selected antimicrobial gas, exemplified by gNO, for a selected period of time suitable for infiltratingly saturating the tympanostomy tubes whereby the gas is sequestered into and within the resin structure comprising the tubes thereby by providing antimicrobial properties to the tympanostomy tubes. Excess gNO is then evacuated from the chamber after which, the gNO-loaded tympanostomy tubes are removed and individually packaged into gas-impermeable containers. In certain embodiments, the chamber may be infiltrated with a semi-porous sealing gaseous material configured to at least partially cross-link with the outer surfaces antimicrobial tympanostomy tubes thereby enabling a further extension of time duration for release of the sequestered gas about the antimicrobial tympanostomy tubes. The chamber may be controllably infiltrated with the semi-porous sealing gaseous material concurrently with evacuation of the antimicrobial gas from the chamber or alternatively, the antimicrobial gas may be completely evacuated from the chamber after which, the semi-porous sealing gaseous material may be infiltrated into the chamber. Excess semi-porous sealing gaseous material is then evacuated from the chamber after which, the gNO-loaded tympanostomy tubes are removed and individually packaged into gas-impermeable containers.

In certain embodiments, gNO-sequestering chelating agents may be incorporated into a suitable selected resin material prior to forming tympanostomy tubes. Suitable gNO-sequestering chelating agents are exemplified by sodium nitrite, nitrosothiols, dipyridoxyl chelating agents, L-arginine, organic nitrates, organic nitrites, thionitrates, thionitrites, N-oxo-N-nitrosamines, N-nitrosamines, sydnonimines, 2-hydroxyimino-5-nitro-alkenamides, diazeniurn diolates, oxatriazolium compounds, oximes, syndomines, molsidomine and derivatives thereof, pirsidomine, furoxanes, nitrosonium salts, and the like, and combinations thereof. A suitable amount of a selected gNO-sequestering chelating agent is placed into a sealable chamber which is then saturated with gNO. A suitable amount of the gNO-loaded chelating agent is then thoroughly intermixed and commingled with a selected resin material after which, the resin material is processed into tympanostomy tubes using methods known to those skilled in these arts. The tympanostomy tubes comprising interspersed therethrough gNO-loaded chelating agent, are then sealably packaged into gas-impermeable containers.

In certain embodiments, an antimicrobial gas-releasing coating may be provided onto the outer surfaces, and optionally on to the inner surfaces, of NO gas-permeated tympanostomy tubes. For example, NO gas-releasing coatings can be provided by applying to the NO gas-permeated tympanostomy tubes, a composition comprising a N₂O₂ ⁻ functional group that will bind to the cured resin material comprising the tympanostomy tubes. Suitable exemplary compounds comprising N₂O₂ ⁻ functional groups are disclosed in U.S. Pat. No. 5,525,357. Other suitable exemplary coating compositions for providing NO gas-releasing coatings onto NO gas-permeated tympanostomy tubes include among others, NO-releasing intramolecular salts known as zwitterions having the general formula 2RN[N(O)NO⁻(CH₂), NH₂ ⁺R′, and S-nitrosothiols.

The antimicrobial gas-permeated tympanostomy tubes described herein can be surgically implanted using well-known procedures, through a patient's tympanic membrane such that one end of the tympanostomy tube extends into the patient's middle ear cavity while the other end of the tube extends through the tympanic membrane into the outer ear cavity. The antimicrobial gas sequestered within the resin material comprising the implanted tympanostomy tube will slowly diffuse from and about the tube thereby alleviating and/or preventing post-operative microbial infections normally associated with these types of tubes and without adverse toxicology reactions exemplified by irritation and inflammation, of otologic tissues. Contact with moisture will expedite the release of gNO sequestered within and coated onto the antimicrobial tympanostomy tubes. Furthermore, provision of NO gas-releasing coatings on the outer surfaces of the tubes, and optionally on their inner surfaces, will inhibit and prevent the formation of biofilms thereon.

EXAMPLES Example 1

A plurality of vent tubes comprising a polytetrafluoroethylene (PTFE) substrate (1.25 mm Sheehy collar buttons, catalog number 23-40300; Inovotec International Inc., Jacksonville, Fla., USA) were placed into gas-ventable Petri dishes. A suitable cather was used to connect the Petri dishes to a manifold connected to a cylinder containing gNO manufactured by Airgas (Chicago Ill., USA). The manifold was provided with a gas flow controller adjusted to deliver 22,000 ppm of gNO to each Petri dish at a flow rate of 30 cc min⁻¹ for a period of 22 h. After the gNO-charging process was completed, the gNO-charged PTFE vent tubes were stored in gas-impermeable containers. All handling of the vent tubes after the gNO-charging process was completed, was done using aseptic techniques.

Stock cultures of Streptococcus pyogenes (ATCC #51878), Streptococcus pneumonia (ATCC #10015), Moraxella catarrhalis (ATCC #25240), and Haemophilus influenzae (ATCC #35540) were maintained on nutrient agar. Broth cultures of each microorganism were prepared by inoculating a test tube containing 10 mL of Brain Heart Infusion broth with a colony picked from a stock culture plate. The inoculated test tubes were cultured for 12 h to 18 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂. The cultures were then diluted with fresh Brain Heart Infusion broth to an OD₆₀₀ reading of 0.5. Each broth culture thus prepared contained 10⁷ to 10⁸ colony-forming units (CFU) mL⁻¹. All handling of the microbial cultures was done using aseptic techniques.

All wells in a 24-well plate received 1 mL of broth culture of a selected microorganism prepared as described above. Each of 12 wells received 1 gNO-charged PTFE vent tube prepared as described above. Each of the remaining 12 wells received 1 sterile PTFE vent tube as supplied by the manufacturer. The tubes were incubated in the broth cultures contained in the 24-well plates for about 1 min after which, each tube was removed from its broth culture and transferred to a quadrant in a quadrant Petri dish. The quadrant Petri dishes were maintained for 7 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂. Individual tubes were removed from the quadrant Petri dishes after 3 h and 7 h of incubation, and were each placed into a microtubes containing 30 μL of sterile phosphate-buffered saline (PBS) and vortexed. The PBS was then pipetted onto a nutrient agar plate and spread across the agar surface. The inoculated plates were then incubated for 24 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂ after which, the plates were removed and the numbers of CFU units appearing thereon were quantified. The results are shown in FIGS. 1-4. The data show that exposure of S. pyogenes (FIGS. 1(a) and 1(b)), S. pneumonia (FIGS. 2(a) and 2(b)), M. catarrhalis (FIGS. 3(a) and 3(b)), and H. influenzae (FIGS. 4(a) and 4(b)) to gNO-charged vent tubes reduced the proliferation of each of the microbial species tested.

Example 2

A plurality of vent tubes comprising a PTFE substrate (Armstrong Beveled vent tube Grommet-type 1.14 mm I.D. Fluorplastic, from Gyrus ACMI, catalog number 140242; Inovotec International Inc., Jacksonville, Fla., USA) were placed into gas-ventable Petri dishes. A suitable cather was used to connect the Petri dishes to a manifold connected to a cylinder containing gNO manufactured by Airgas (Chicago Ill., USA). The manifold was provided with a gas flow controller adjusted to deliver 22,000 ppm of gNO to each Petri dish at a flow rate of 30 cc min⁻¹ for a period of 22 h. After the gNO-charging process was completed, the gNO-charged PTFE vent tubes were stored in gas-impermeable containers. All handling of the vent tubes after the gNO-charging process was completed, was done using aseptic techniques.

A stock culture of methicillin-resistant Staphylococcus aureus (MRSA; ATCC #700698), was maintained on nutrient agar. MSRA is a S. aureus strain that is known to be resistant to a number of broad-spectrum antibiotics commonly used to treat it. MRSA broth cultures were prepared by inoculating a plurality of test tubes containing 10 mL of Brain Heart Infusion broth with a colony picked from a stock culture plate. The inoculated test tubes were cultured for 12 h to 18 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂. The cultures were then diluted with fresh Brain Heart Infusion broth to an OD₆₀₀ reading of 0.5. Each broth culture thus prepared contained about 05 CFU mL⁻¹. All handling of the microbial cultures was done using aseptic techniques.

All wells in a 24-well plate received 1 mL of a MSRA broth culture prepared as described above. Each of 12 wells received 1 gNO-charged PTFE vent tube prepared as described above. Each of the remaining 12 wells received 1 sterile PTFE vent tube as supplied by the manufacturer. The tubes were incubated in the broth cultures contained in the 24-well plates for about 1 min after which, each tube was removed from its broth culture and transferred to a quadrant in a quadrant Petri dish. The quadrant Petri dishes were maintained for 7 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂. Individual tubes were removed from the quadrant Petri dishes after 3 h and 7 h of incubation, and were each placed into a microtubes containing 30 μL of sterile phosphate-buffered saline (PBS) and vortexed. The PBS was then pipetted onto a nutrient agar plate and spread across the agar surface. The inoculated plates were then incubated for 24 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂ after which, the plates were removed and the numbers of CFU units appearing thereon were quantified. The results are shown in Fig. The data show that exposure of methicillin-resistant Staphylococcus aureus (FIGS. 5(a) and 5(b)) to gNO-charged vent tubes reduced the proliferation of this microbial species.

Example 3

A first plurality of vent tubes comprising a silicon substrate (T-Tube, Silicon Myringotomy Tube, 23-50600; Invotec International Inc., Jacksonville, Fla., US) and a second plurality of vent tubes a PTFE substrate (Sheehy Collar Button, Fluoroplastic Myringotomy Tube, 23-40300; Inovotec International Inc., Jacksonville, Fla., USA) were placed into gas-ventable Petri dishes. A suitable cather was used to connect the Petri dishes to a manifold connected to a cylinder containing gNO manufactured by Airgas (Chicago Ill., USA). The manifold was provided with a gas flow controller adjusted to deliver 22,000 ppm of gNO to each Petri dish at a flow rate of 30 cc min⁻¹ for a period of 22 h. After the gNO-charging process was completed, the gNO-charged silicon vent tubes and PTFE vent tubes were stored in gas-impermeable containers. All handling of the vent tubes after the gNO-charging process was completed, was done using aseptic techniques.

A stock culture of a Staphylococcus aureus (ATCC #25923), was maintained on nutrient agar. S. aureus broth cultures were prepared by inoculating a plurality of test tubes containing 10 mL of Brain Heart Infusion broth with a colony picked from a stock culture plate. The inoculated test tubes were cultured for 12 h to 18 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂. The cultures were then diluted with fresh Brain Heart Infusion broth to an OD₆₀₀ reading of 0.5. Each broth culture thus prepared contained about 10⁵ CFU mL⁻¹. All handling of the microbial cultures was done using aseptic techniques.

All wells in a 24-well plate received 1 mL of a S. aureus broth culture prepared as described above. Each of 12 wells received 1 gNO-charged PTFE vent tube prepared as described above. Each of the remaining 12 wells received 1 sterile PTFE vent tube as supplied by the manufacturer. The tubes were incubated in the broth cultures contained in the 24-well plates for about 1 min after which, each tube was removed from its broth culture and transferred to a quadrant in a quadrant Petri dish. The quadrant Petri dishes were maintained for 7 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂. Individual tubes were removed from the quadrant Petri dishes after 3 h and 7 h of incubation, and were each placed into a microtubes containing 30 μL of sterile phosphate-buffered saline (PBS) and vortexed. The PBS was then pipetted onto a nutrient agar plate and spread across the agar surface. The inoculated plates were then incubated for 24 h at 37° C. in an incubator provided with an atmosphere containing about 5% CO₂ after which, the plates were removed and the numbers of CFU units appearing thereon were quantified. The results are shown in Fig. The data show that exposure of S. aureus ATCC #25923 to gNO-charged vent tubes reduced the proliferation of this microbial species on silicon-based vent tubes and on PTFE vent tubes (FIG. 6).

While this invention has been described with respect to the exemplary embodiments, it is to be understood that various alterations and modifications can be made to the configurations and shapes of the antimicrobial tympanostomy tubes, and to methods for saturatingly infiltrating the tubes with a selected antimicrobial gas within the scope of this invention.

Further, the foregoing is merely intended to illustrate various embodiments of the present invention. The specific modifications or characteristics discussed above are not to be construed as limitations on the scope of the invention. It will be apparent to one skilled in the art that various equivalents, changes, and modifications may be made without departing from the scope of the invention, and it is understood that such equivalent embodiments are to be included herein. All references cited herein are incorporated by reference as if fully set forth herein. 

What is claimed is:
 1. An assembly enclosing a device having a portion configured for insertion into a body, comprising: a container that is impermeable to gaseous nitric oxide; and a device having a portion configured for insertion into a body, said portion consisting of a resin material permeable to gaseous nitric oxide, wherein said resin material is controllably saturated with gaseous nitric oxide so as to releasably sequester said nitric oxide gas molecules therein, wherein said device with sequestered gaseous nitric oxide is packaged in said container impermeable to said gaseous nitric oxide.
 2. The assembly of claim 1, wherein said resin material of said device is curable.
 3. The assembly of claim 1, wherein said resin material of said device is microporous.
 4. The assembly of claim 1, wherein said resin material of said device is hydrophobic.
 5. The assembly of claim 1, wherein said resin material of said device is selected from the group consisting of curable silicones, polyvinyl acetates, thermoplastic elastomers, acrylonitrile-butadiene-styrene copolymer rubber, polyurethanes and selected combinations thereof.
 6. The assembly of claim 1, wherein said resin material of said device is configured to be a conduit.
 7. An assembly enclosing an article comprising a device configured for insertion into a body, comprising: a container that is impermeable to gaseous nitric oxide; and an article comprising a device configured for insertion into a body, said device consisting of a resin material permeable to gaseous nitric oxide, wherein said resin material is controllably saturated with gaseous nitric oxide so as to releasably sequester said nitric oxide gas molecules therein, wherein said device with sequestered gaseous nitric oxide is packaged in said container impermeable to said gaseous nitric oxide.
 8. The assembly of claim 7, wherein said resin material of said device is curable.
 9. The assembly of claim 7, wherein said resin material of said device is microporous.
 10. The assembly of claim 7, wherein said resin material of said device is hydrophobic.
 11. The assembly of claim 7, wherein said resin material of said device is selected from the group consisting of curable silicones, polyvinyl acetates, thermoplastic elastomers, acrylonitrile-butadiene-styrene copolymer rubber, polyurethanes and selected combinations thereof.
 12. The assembly of claim 7, wherein said resin material of said device is configured to be a conduit. 